China Manufacturer Hot DIP Galvanised Steel Welded Wire Mesh

High Strength Galvanized Steel Wire is a steel wire with a wide range of applications, which can be used in equipment such as terminal cranes, mining winches and tower cranes.

Send Inquiry

Always customer-oriented, and it's our ultimate goal to get not only by far the most reputable, trustable and honest supplier, but also the partner for Galvanized Steel Coils, Stainless STEEL TUBING, dx53d Coating Steel Coils. Economic globalization and the rapid development of science and technology have created unprecedented technical conditions for the development of our company. Determined to stay vigilant for danger in times of fierce market competition, work hard, continue to implement the brand development strategy, take the road of management and technological innovation, and continuously improve the company's innovation capabilities. We adhere to the business philosophy of 'taking talents as the foundation, relying on science and technology, market-oriented, quality as the pillar and reputation as the backing', and meet the requirements of our customers with high-quality products and perfect and fast after-sales service. Guided by the market, with products as the core, we continue to create various products categories to better satisfy customers' needs.

Product Introduction

High Strength Galvanized Steel Wire is a steel wire with a wide range of applications, which can be used in equipment such as terminal cranes, mining winches and tower cranes. It not only has high strength and good performance, but also has quality assurance. It is the best choice for steel reinforcement applications in engineering construction and industrial manufacturing.

Features

High Strength Galvanized Steel Wire is made of high-quality galvanized steel wire, with high strength, sturdiness and durability, and stronger fatigue resistance. It has a smooth surface, no burrs, and will not hurt your hands. It has strong bearing capacity, abrasion resistance , and the quality is guaranteed. Please rest assured to buy.

Diameter: 1.8mm – 4.0mm

Package: Coil(50kg-500kg), Drum, Z2, Z3

Standard: ASTM B498, GB/T 3428(G1A-G5A)

Application: High strength galvanized steel wire for Round wire concentric lay overhead electrical stranded conductors,

1 Grade Galvanized Steel Wire

Specified Diameter MM		Mm Permissible variation	Stress at 1% Extension, min, Mpa	Ultimate Tensile Strength, Min Mpa	Elongation in 250mm min, %	Wrap Test of Cylindrical mandrel dia mm	Twist Test No. min
From	To		Stress at 1% Extension, min, Mpa	Ultimate Tensile Strength, Min Mpa
From	To		Zinc Coating Class A
1.80	2.25	±0.03	1170	1340	3	1D	18
2.25	2.75	±0.04	1140	1310	3	1D	16
2.75	3.00	±0.05	1140	1310	3.5	1D	16
3.00	3.50	±0.05	1100	1290	3.5	1D	14
3.50	4.00	±0.06	1100	1290	4	1D	12

2 Grade Galvanized Steel Wire

D Specified Diameter MM		Mm Permissible Variation	Stress at 1% Extension, min Mpa	Ultimate Tensile Strength, Min Mpa	Elongation in 250mm min, %	Wrap Test of Cylindrical mandrel dia. mm	Twist Test No. min
From	To		Stress at 1% Extension, min Mpa	Ultimate Tensile Strength, Min Mpa
From	To		Zinc Coating Class A
1.80	2.25	±0.03	1310	1450	2.5	3D	16
2.25	2.75	±0.04	1280	1410	2.5	3D	16
2.75	3.00	±0.05	1280	1410	3.0	4D	16
3.00	3.50	±0.05	1240	1410	3.0	4D	14
3.50	4.00	±0.06	1170	1380	3.0	4D	12

3 Grade Galvanized Steel Wire

D Specified Diameter. MM		Mm Permissible Variation	Stress at 1% Extension, Min Mpa	Ultimate Tensile Strength, Min Mpa	Elongation in 250mm min, %	Wrap test of Cylindrical mandrel dia. mm	Twist test No. min
From	To		Stress at 1% Extension, Min Mpa	Ultimate Tensile Strength, Min Mpa
From	To		Zinc Coating Class A
1.80	2.25	±0.03	1450	1620	2.0	4D	14
2.25	2.75	±0.04	1410	1590	2.0	4D	14
2.75	3.00	±0.05	1410	1590	2.5	4D	12
3.00	3.50	±0.05	1380	1550	2.5	4D	12
3.50	4.00	±0.06	1340	1520	2.5	4D	10

4 Grade Galvanized Steel Wire

D Specified Diameter. MM		Mm Permissible Variation	Stress at 1% Extension, Min Mpa	Ultimate Tensile Strenght, Min Mpa	Elongation in 250mm min, %	Wrap test of Cylindrical mandrel dia. mm	Twist test No. min
From	To		Stress at 1% Extension, Min Mpa	Ultimate Tensile Strenght, Min Mpa
From	To		Zinc Coating Class A
1.80	2.25	±0.03	1580	1870	3.0	4D	12
2.25	2.75	±0.04	1580	1820	3.0	4D	12
2.75	3.00	±0.05	1550	1820	3.5	4D	12
3.00	3.50	±0.05	1550	1770	3.5	4D	12
3.50	4.00	±0.06	1500	1720	3.5	4D	10

5 Grade Galvanized Steel Wire

D Specified Diameter. MM		Mm Permissible Variation	Stress at 1% Extension, Min Mpa	Ultimate Tensile Strenght, Min Mpa	Elongation in 250mm min, %	Wrap test of Cylindrical mandrel dia. mm	Twist test No. min
From	To		Stress at 1% Extension, Min Mpa	Ultimate Tensile Strenght, Min Mpa
From	To		Zinc Coating Class A
1.80	2.25	±0.03	1600	1960	3.0	4D	12
2.25	2.75	±0.04	1600	1910	3.0	4D	12
2.75	3.00	±0.05	1580	1910	3.5	4D	12
3.00	3.50	±0.05	1580	1870	3.5	4D	12
3.50	4.00	±0.06	1550	1820	3.5	4D	10

Zinc Coating

D Specified Diameter. mm		Area Density of Coating, min, of Uncoated Wire Surface, g/㎡
From	To	Class A	Class B
1.8	2.25	215	/
2.25	3.00	230	/
3.00	3.50	245	/
3.50	4.00	260	/

Production Equipment

The 300,000-ton automatic tunnel-type continuous pretreatment line (production line) is controlled by the PLC program control system, and is subjected to surface treatment processes such as pickling, dipping, rinsing, phosphating, warm washing, saponification, and drying.

8 straight-type wire drawing machines, the pickled phosphating saponified wire rods are drawn through multiple passes to reach the required diameter and wound up onto the spool.

The steel wire is discharged through the pay-off machine and enters the electrolytic alkali washing tank for degreasing (removing the lubricating film during drawing)

The steel wire is degreased and cleaned by electrolytic alkali washing tank, pickled, washed, and then enters the plating bath, and then dried to enter the hot-dip galvanizing pot.

The excess zinc on the surface of the steel wire was scraped back to the zinc pot by a nitrogen wiping device, and a zinc layer having a smooth surface was obtained, and then the cooling jet formed by the four water nozzles cooled the molten zinc into solid zinc. Then enter the wire take-up machine through the branch line guiding device.

Through the guiding device and take-up machine,leading to two type of packing.One is the hollow packing,the other one is spool packing.

The steel wire is wound from the 1000 type wheel to the 400, 500 or 630 type of wheel. The process should pay attention to the steel wire strength grade, wire diameter and wire length. If the error occurs, the steel strand can not be delivered.

4 sets 1x7 stranding machine and 1 set 1x19 stranding machine.

Testing Equipments

Our company has complete and advanced testing facilities and high qualified inspection technicians. Each process, from the materials, semi-products, finished products, to the production implement, is totally under a strict quality control system to guarantee the final performances of all the products.

1.Electronic Tensile Testing Machine; （100T） Hydraulic Universal Testing Machine; Torsion Testing Machine; Metallographic Microscope

2.Chemical Composition Analyzer; Bend Testing Machine; Wrap Testing Machine; Fatigue Testing Machine

Our goal is to continuously provide high-quality China Manufacturer Hot DIP Galvanised Steel Welded Wire Mesh and services that exceed customer expectations, and to promote the development of the industry with customers all over the world. Flexible business channels, superior environment, good marketing network, strict management of purchase, sale and storage have laid a solid foundation for our business development. We take employees' feelings as the starting point, create a home atmosphere for employees and enhance their sense of belonging.

Hot Tags: high strength galvanized steel wire, China high strength galvanized steel wire suppliers, manufacturers, factory, high pressure compression stainless steel fittings, steel strand 15 7 mm, Hot rolled Galvanized Steel Sheets, 321 stainless steel pipe, stainless steel coupling elbow fittings, HOT ROLLED STAINLESS STEEL COIL